OEM China Malaysia Graphite Electrode - 300mm UHP Electrode – Hexi
OEM China Malaysia Graphite Electrode - 300mm UHP Electrode – Hexi Detail:
Application
Graphite electrodes are widely used for production of alloy steels, metal and other nonmetallic materials, etc.
* DC electric arc furnace.
* AC electric arc furnace.
* Submerged arc furnace.
* Ladle furnace.
| Comparison Technical Specification for UHP Graphite Electrode 12″ | ||
| Electrode | ||
| Item | Unit | Supplier Spec |
| Typical Characteristics of Pole | ||
| Nominal Diameter | mm | 300 |
| Max Diameter | mm | 307 |
| Min Diameter | mm | 299 |
| Nominal Length | mm | 1600/1800 |
| Max Length | mm | 1700/1900 |
| Min Length | mm | 1500/1700 |
| Bulk Density | g/cm3 | 1.68-1.73 |
| transverse strength | MPa | ≥12.0 |
| Young’ Modulus | GPa | ≤13.0 |
| Specific Resistance | µΩm | 4.8-5.8 |
| Maximum current density | KA/cm2 | 20-30 |
| Current Carrying Capacity | A | 15000-22000 |
| (C.T.E) | 10-6℃ | ≤1.2 |
| ash content | % | ≤0.2 |
| Typical Characteristics of Nipple (4TPI) | ||
| Bulk Density | g/cm3 | 1.78-1.84 |
| transverse strength | MPa | ≥22.0 |
| Young’ Modulus | GPa | ≤18.0 |
| Specific Resistance | µΩm | 3.4～4.0 |
| (C.T.E) | 10-6℃ | ≤1.0 |
| ash content | % | ≤0.2 |
Product detail pictures:
Related Product Guide:
We take pleasure in an exceptionally excellent status between our buyers for our superb merchandise good quality, aggressive price tag and the greatest support for OEM China Malaysia Graphite Electrode - 300mm UHP Electrode – Hexi, The product will supply to all over the world, such as: Salt Lake City, Lithuania, Japan, To get more information about us as well as see all our products, please visit our website. To get more information please feel free to let us know. Thank you very much and wish your business always be great!
By Grace from Georgia - 2017.12.09 14:01
The company's products very well, we have purchased and cooperated many times, fair price and assured quality, in short, this is a trustworthy company!
By Polly from USA - 2017.05.02 11:33